Analysis of suitability of TPP ash-slag waste as materials for hydrogen fuel storage

The current trends in energy were described, the main of which is the use of alternative energy sources, especially hydrogen. The most common methods of hydrogen accumulation were proposed: accumulation of compressed gaseous hydrogen in high-pressure tanks; accumulation of liquid hydrogen in cryogenic tanks; storing hydrogen in a chemically bound state; accumulation of gaseous hydrogen in carriers with a high specific surface area. Based on the combination of advantages and disadvantages, the most promising methods of accumulation were selected: storage of liquid hydrogen and storage of hydrogen in carriers with a high specific surface area. The main requirement for materials for hydrogen storage by these methods was revealed – a high specific surface area. Prospects for the development of waste-free low-emission technologies due to the recycling of secondary raw materials and the development of low-temperature technologies for the synthesis of functional and structural materials were substantiated. The applicability of large-scale ash and slag waste from coal-fired thermal power plants as a raw material for obtaining materials by low-temperature technologies was shown. The traditional ways of using ash and slag waste as a raw material, active additive and filler in the production of cements were described. Modern technologies for the production of innovative materials with a unique set of properties were presented, namely carbon nanotubes, silica aerogel and geopolymer materials. The prospect of using geopolymer matrices as a precursor for the synthesis of a number of materials was described; the most promising type of materials was selected – geopolymer foams, which are mainly used as sorbents for purifying liquids and gases or accumulating target products, as well as heat-insulating materials. The possibility of obtaining products of any shape and size on the basis of geopolymer matrices without high-temperature processing was shown. The special efficiency of the development of the technology of porous granules and powders obtained from a geopolymer precursor using various methods was substantiated. The obtained granules can be used in the following hydrogen storage technologies: direct accumulation of hydrogen in porous granules; creation of insulating layers for liquid hydrogen storage units.     

碳脱氧在钢包顶渣改质中的应用

 为了进一步降低夹杂物缺陷并提高产品质量,基于碳脱氧进行了钢包顶渣改质的研究。冷轧产品的生产工艺为铁水预处理→转炉→RH精炼→连铸,为减少钢中夹杂物质量分数,需要进行钢包顶渣改质,同时降低钢包顶渣TFe质量分数。采用粒碳部分替代铝渣球的方法进行基于碳脱氧工艺的钢包顶渣改质,试验结果表明,顶渣改质效果良好,在顶渣TFe质量分数、中间包钢水游离氧明显降低的同时铸坯中Al₂O₃夹杂物得到优化;“30 kg粒渣+铝渣球”工艺降低生产成本5.16元/t(钢)。     

Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to [AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and [AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.     

Effect of steel slag on 3D concrete printing of geopolymer with quaternary binders

A new type of 3D-printable ‘one-part’ geopolymer was synthesized with fly ash (FA), granulated blast furnace slag (GBFS), steel slag (SS) and flue gas desulfurization gypsum (FGD). The effects of SS content (0–40%) on the rheological properties, 3D-printability, mechanical anisotropy and reaction kinetics of geopolymer were investigated. The yield stress and plastic viscosity monotonically decreased with the increasing SS content. Contrarily, the geopolymer with 10% of SS presented better extrudability, buildability and mechanical strength than those with 0, 20%, 30% and 40% of SS. This was mainly attributed to the conflicting influence of SS on geopolymerization, of which the OH^? produced by hydration of SS raised the alkalinity of the reaction system and accelerated the dissolution of SiO₄^4? and AlO₄^5?, while the low reactivity prohibited the following polymerization process. Furthermore, the 3D-printed geopolymer presented more compact microstructure and less mechanical anisotropy thanks to the crosslinking of morphologically complementary products, including N(C)-A-S-H, C–S–H, AFt and CH, formed via synergistic reaction of FA-GBFS-SS-FGD system.     

Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

上水口环形吹氩对中间包内渣眼形成的影响

 中间包上水口环形吹氩可以在塞棒周围形成清洗钢液的环形气幕，同时部分氩气泡随钢液进入上水口内，可以减少非金属夹杂物在水口内壁的黏附，起到防止水口堵塞的作用。然而，不合理的吹氩量会导致中间包内液面渣层受过强的气液羽流冲击而形成渣眼，使得钢液裸露并发生二次氧化，严重影响铸坯质量。采用标准 k ε 湍流模型研究中间包内流体流动，采用DPM模型和VOF模型耦合方法，研究上水口环形吹氩条件下渣眼的形成及演化规律。结果表明，上水口环形吹氩在塞棒周围形成较强的上升流，塞棒上部邻近区域存在多个涡流区；在钢液涡流的影响下，中间包液渣下层远离塞棒区域，上层向塞棒区域迁移；随着吹氩量的增大，平均湍动能增大，塞棒附近钢液速度逐渐增大，钢渣界面钢液速度先增大后减小，渣眼边缘钢液速度先增大后减小然后再增大，速度与垂直方向夹角逐渐减小；增大吹氩量，中间包熔池液面形成以塞棒为中心的渣眼，渣眼面积逐渐增大。试验条件下不产生渣眼的临界吹氩量为4.2 L/min，对应的钢渣界面最大速度为0.247 m/s，与垂直方向夹角为70°。     

Preparation of high strength foam ceramics from sand shale and steel slag

Foam ceramics with high strength were successfully fabricated by using sand shale and steel slag as the major materials and SiC as foam agent. The influence of raw materials ratio and heat treatment temperatures on crystalline phases, porosity, mechanical properties and pore structures was investigated via XRF, XRD, SEM, DTA-TG, Micro-CT. The results indicate that the raw materials composed of 94 wt% sand shale and 6 wt% steel slag enable the fabrication of foam ceramics possessing strength of 29.98 MPa, bulk density of 0.821 g/cm³, total porosity of 67.22%, closed porosity of 55.27% and thermal conductivity of 0.08 W/(m·K). Micro-CT result shows that the pores with an average size of 267.05 μm are isolated. Pore wall thickness conforms to normal distribution, and it ranges from 18 to 42 μm. The superior property makes it promising high-strength and lightweight material in application fields, including thermal insulation materials and lightweight building materials.